|Preferred IUPAC name
3D model (JSmol)
CompTox Dashboard (EPA)
|Molar mass||44.08 g/mol|
|Appearance||brown-black glassy solid|
|Melting point||1,702 °C (3,096 °F; 1,975 K)|
|Boiling point||1,880 °C (3,420 °F; 2,150 K)|
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
|what is ?)(|
Silicon monoxide is the chemical compound with the formula SiO where silicon is present in the oxidation state +2. In the vapour phase it is a diatomic molecule. It has been detected in stellar objects and it has been described as the most common oxide of silicon in the universe.
When SiO gas is cooled rapidly, it condenses to form a brown/black polymeric glassy material, (SiO)n, which is available commercially and used to deposit films of SiO. Glassy (SiO)n is air- and moisture-sensitive. Its surface readily oxidizes in air at room temperature, giving an SiO2 surface layer that protects the material from further oxidation. However, (SiO)n irreversibly disproportionates into SiO2 and Si in a few hours between 400 and 800°C, and very rapidly between 1,000 and 1,440°C, although the reaction does not go to completion.
The first precise report on the formation of SiO was in 1887 by the chemist Charles F. Maybery (1850–1927) at the Case School of Applied Science in Cleveland. Maybery claimed that SiO formed as an amorphous greenish-yellow substance with a vitreous luster when silica was reduced with charcoal in the absence of metals in an electric furnace. The substance was always found at the interface between the charcoal and silica particles. By investigating some of the chemical properties of the substance, its specific gravity, and a combustion analysis, Maybery deduced that the substance must be SiO. The equation representing the partial chemical reduction of SiO2 with C can be represented as:
Complete reduction of SiO2 with twice the amount of carbon yields elemental silicon and twice the amount of carbon monoxide. In 1890, the German chemist Clemens Winkler (the discoverer of germanium) was the first to attempt to synthesize SiO by heating silicon dioxide with silicon in a combustion furnace.
However, Winkler was not able to produce the monoxide since the temperature of the mixture was only around 1000°C. The experiment was repeated in 1905 by Henry Noel Potter (1869–1942), a Westinghouse engineer. Using an electric furnace, Potter was able to attain a temperature of 1700°C and observe the generation of SiO. Potter also investigated the properties and applications of the solid form of SiO.
Because of the volatility of SiO, silica can be removed from ores or minerals by heating them with silicon to produce gaseous SiO in this manner. However, due to the difficulties associated with accurately measuring its vapor pressure, and because of the dependency on the specifics of the experimental design, various values have been reported in the literature for the vapor pressure of SiO (g). For the pSiO above molten silicon in a quartz (SiO2) crucible at the melting point of silicon, one study yielded a value of 0.002 atm. For the direct vaporization of pure, amorphous SiO solid, 0.001 atm has been reported. For a coating system, at the phase boundary between SiO2 and a silicide, 0.01 atm was reported.
Silica itself, or refractories containing SiO2, can be reduced with H2 or CO at high temperatures, e.g.:
As the SiO product volatilizes off (is removed), the equilibrium shifts to the right, resulting in the continued consumption of SiO2. Based on the dependence of the rate of silica weight loss on the gas flow rate normal to the interface, the rate of this reduction appears to be controlled by convective diffusion or mass transfer from the reacting surface.
Silicon monoxide molecules have been trapped in an argon matrix cooled by helium. In these conditions, the SiO bond length is between 148.9 pm and 151 pm. This bond length is similar to the length of Si=O double bonds (148 pm) in the matrix-isolated linear molecule SiO
2 (O=Si=O), indicative of the absence of a triple bond as in carbon monoxide. However, the SiO triple bond has a calculated bond length of 150 pm and a bond energy of 794 kJ/mol, which are also very close to those reported for SiO. The SiO double bond structure is, notably, an exception to Lewis' octet rule for molecules composed of the light main group elements, whereas the SiO triple bond satisfies this rule. That anomaly not withstanding, the observation that monomeric SiO is short-lived and that (SiO)'n' oligomers with 'n' = 2,3,4,5 are known, all having closed ring structures in which the silicon atoms are connected through bridging oxygen atoms (i.e. each oxygen atom is singly bonded to two silicon atoms; no Si-Si bonds), suggests the Si=O double bond structure, with a hypovalent silicon atom, is likely for the monomer.
Condensing molecular SiO in argon matrix together with fluorine, chlorine or carbonyl sulfide (COS), followed by irradiation with light, produces the planar molecules OSiF
2 (with Si-O distance 148 pm) and OSiCl
2 (Si-O 149 pm), and the linear molecule OSiS (Si-O 149 pm, Si-S 190 pm).
Matrix-isolated molecular SiO reacts with oxygen atoms generated by microwave discharge to produce molecular SiO
2 which has a linear structure.
When metal atoms (such as Na, Al, Pd, Ag, and Au) are co-deposited with SiO, triatomic molecules are produced with linear (AlSiO and PdSiO), non-linear (AgSiO and AuSiO), and ring (NaSiO) structures.
Potter reported SiO solid as yellowish-brown in color and as being an electrical and thermal insulator. The solid burns in oxygen and decomposes water with the liberation of hydrogen. It dissolves in warm alkali hydroxides and in hydrofluoric acid. Even though Potter reported the heat of combustion of SiO to be 200 to 800 calories higher than that of an equilibrium mixture of Si and SiO2 (which could, arguably, be used as evidence that SiO is a unique chemical compound), some studies characterized commercially available solid silicon monoxide materials as an inhomogeneous mixture of amorphous SiO2 and amorphous Si with some chemical bonding at the interface of the Si and SiO2 phases. Recent spectroscopic studies in a correlation with Potter's report suggest that commercially available solid silicon monoxide materials can not be considered as an inhomogeneous mixture of amorphous SiO2 and amorphous Si.