|Appearance||silvery lustrous gray|
|Standard atomic weight Ar, std(Sb)||121.760(1)|
|Antimony in the periodic table|
|Atomic number (Z)||51|
|Group||group 15 (pnictogens)|
|Electron configuration||[Kr] 4d10 5s2 5p3|
|Electrons per shell||2, 8, 18, 18, 5|
|Phase at STP||solid|
|Melting point||903.78 K (630.63 °C, 1167.13 °F)|
|Boiling point||1908 K (1635 °C, 2975 °F)|
|Density (near r.t.)||6.697 g/cm3|
|when liquid (at m.p.)||6.53 g/cm3|
|Heat of fusion||19.79 kJ/mol|
|Heat of vaporization||193.43 kJ/mol|
|Molar heat capacity||25.23 J/(mol·K)|
|Oxidation states||−3, −2, −1, 0, +1, +2, +3, +4, +5 (an amphoteric oxide)|
|Electronegativity||Pauling scale: 2.05|
|Atomic radius||empirical: 140 pm|
|Covalent radius||139±5 pm|
|Van der Waals radius||206 pm|
|Spectral lines of antimony|
|Speed of sound thin rod||3420 m/s (at 20 °C)|
|Thermal expansion||11 µm/(m·K) (at 25 °C)|
|Thermal conductivity||24.4 W/(m·K)|
|Electrical resistivity||417 nΩ·m (at 20 °C)|
|Magnetic susceptibility||−99.0·10−6 cm3/mol|
|Young's modulus||55 GPa|
|Shear modulus||20 GPa|
|Bulk modulus||42 GPa|
|Brinell hardness||294–384 MPa|
|Discovery||Arabic alchemists (before AD 815)|
|Main isotopes of antimony|
Antimony is a chemical element with the symbol Sb (from Latin: stibium) and atomic number 51. A lustrous gray metalloid, it is found in nature mainly as the sulfide mineral stibnite (Sb2S3). Antimony compounds have been known since ancient times and were powdered for use as medicine and cosmetics, often known by the Arabic name kohl. Metallic antimony was also known, but it was erroneously identified as lead upon its discovery. The earliest known description of the metal in the West was written in 1540 by Vannoccio Biringuccio.
For some time, China has been the largest producer of antimony and its compounds, with most production coming from the Xikuangshan Mine in Hunan. The industrial methods for refining antimony are roasting and reduction with carbon or direct reduction of stibnite with iron.
The largest applications for metallic antimony are an alloy with lead and tin and the lead antimony plates in lead–acid batteries. Alloys of lead and tin with antimony have improved properties for solders, bullets, and plain bearings. Antimony compounds are prominent additives for chlorine and bromine-containing fire retardants found in many commercial and domestic products. An emerging application is the use of antimony in microelectronics.
Antimony is a member of group 15 of the periodic table, one of the elements called pnictogens, and has an electronegativity of 2.05. In accordance with periodic trends, it is more electronegative than tin or bismuth, and less electronegative than tellurium or arsenic. Antimony is stable in air at room temperature, but reacts with oxygen if heated to produce antimony trioxide, Sb2O3.:758
Antimony is a silvery, lustrous gray metalloid with a Mohs scale hardness of 3, which is too soft to make hard objects; coins of antimony were issued in China's Guizhou province in 1931 but the durability was poor and the minting was soon discontinued. Antimony is resistant to attack by acids.
Four allotropes of antimony are known: a stable metallic form and three metastable forms (explosive, black and yellow). Elemental antimony is a brittle, silver-white shiny metalloid. When slowly cooled, molten antimony crystallizes in a trigonal cell, isomorphic with the gray allotrope of arsenic. A rare explosive form of antimony can be formed from the electrolysis of antimony trichloride. When scratched with a sharp implement, an exothermic reaction occurs and white fumes are given off as metallic antimony forms; when rubbed with a pestle in a mortar, a strong detonation occurs. Black antimony is formed upon rapid cooling of antimony vapor. It has the same crystal structure as red phosphorus and black arsenic; it oxidizes in air and may ignite spontaneously. At 100 °C, it gradually transforms into the stable form. The yellow allotrope of antimony is the most unstable. It has only been generated by oxidation of stibine (SbH3) at −90 °C. Above this temperature and in ambient light, this metastable allotrope transforms into the more stable black allotrope.
Elemental antimony adopts a layered structure (space group R3m No. 166) in which layers consist of fused, ruffled, six-membered rings. The nearest and next-nearest neighbors form an irregular octahedral complex, with the three atoms in each double layer slightly closer than the three atoms in the next. This relatively close packing leads to a high density of 6.697 g/cm3, but the weak bonding between the layers leads to the low hardness and brittleness of antimony.:758
Antimony has two stable isotopes: 121Sb with a natural abundance of 57.36% and 123Sb with a natural abundance of 42.64%. It also has 35 radioisotopes, of which the longest-lived is 125Sb with a half-life of 2.75 years. In addition, 29 metastable states have been characterized. The most stable of these is 120m1Sb with a half-life of 5.76 days. Isotopes that are lighter than the stable 123Sb tend to decay by β+ decay, and those that are heavier tend to decay by β− decay, with some exceptions.
The abundance of antimony in the Earth's crust is estimated to be 0.2 to 0.5 parts per million, comparable to thallium at 0.5 parts per million and silver at 0.07 ppm. Even though this element is not abundant, it is found in more than 100 mineral species. Antimony is sometimes found natively (e.g. on Antimony Peak), but more frequently it is found in the sulfide stibnite (Sb2S3) which is the predominant ore mineral.
Antimony trioxide is formed when antimony is burnt in air. In the gas phase, the molecule of the compound is Sb
6, but it polymerizes upon condensing. Antimony pentoxide (Sb
10) can be formed only by oxidation with concentrated nitric acid. Antimony also forms a mixed-valence oxide, antimony tetroxide (Sb
4), which features both Sb(III) and Sb(V). Unlike oxides of phosphorus and arsenic, these oxides are amphoteric, do not form well-defined oxoacids, and react with acids to form antimony salts.
Antimonous acid Sb(OH)
3 is unknown, but the conjugate base sodium antimonite ([Na
4) forms upon fusing sodium oxide and Sb
6.:763 Transition metal antimonites are also known.:122 Antimonic acid exists only as the hydrate HSb(OH)
6, forming salts as the antimonate anion Sb(OH)−
6. When a solution containing this anion is dehydrated, the precipitate contains mixed oxides.:143
Many antimony ores are sulfides, including stibnite (Sb
3), pyrargyrite (Ag
3), zinkenite, jamesonite, and boulangerite.:757 Antimony pentasulfide is non-stoichiometric and features antimony in the +3 oxidation state and S-S bonds. Several thioantimonides are known, such as [Sb
It is Lewis acidic and readily accepts fluoride ions to form the complex anions SbF−
4 and SbF2−
5. Molten SbF
3 is a weak electrical conductor. The trichloride SbCl
3 is prepared by dissolving Sb
3 in hydrochloric acid:
The pentahalides SbF
5 and SbCl
5 have trigonal bipyramidal molecular geometry in the gas phase, but in the liquid phase, SbF
5 is polymeric, whereas SbCl
5 is monomeric.:761 SbF
5 is a powerful Lewis acid used to make the superacid fluoroantimonic acid ("H2SbF7").
Compounds in this class generally are described as derivatives of Sb3−. Antimony forms antimonides with metals, such as indium antimonide (InSb) and silver antimonide (Ag
3Sb).:760 The alkali metal and zinc antimonides, such as Na3Sb and Zn3Sb2, are more reactive. Treating these antimonides with acid produces the highly unstable gas stibine, SbH
Stibine can also be produced by treating Sb3+
salts with hydride reagents such as sodium borohydride. Stibine decomposes spontaneously at room temperature. Because stibine has a positive heat of formation, it is thermodynamically unstable and thus antimony does not react with hydrogen directly.
Organoantimony compounds are typically prepared by alkylation of antimony halides with Grignard reagents. A large variety of compounds are known with both Sb(III) and Sb(V) centers, including mixed chloro-organic derivatives, anions, and cations. Examples include Sb(C6H5)3 (triphenylstibine), Sb2(C6H5)4 (with an Sb-Sb bond), and cyclic [Sb(C6H5)]n. Pentacoordinated organoantimony compounds are common, examples being Sb(C6H5)5 and several related halides.
An artifact, said to be part of a vase, made of antimony dating to about 3000 BC was found at Telloh, Chaldea (part of present-day Iraq), and a copper object plated with antimony dating between 2500 BC and 2200 BC has been found in Egypt. Austen, at a lecture by Herbert Gladstone in 1892, commented that "we only know of antimony at the present day as a highly brittle and crystalline metal, which could hardly be fashioned into a useful vase, and therefore this remarkable 'find' (artifact mentioned above) must represent the lost art of rendering antimony malleable."
The British archaeologist Roger Moorey was unconvinced the artifact was indeed a vase, mentioning that Selimkhanov, after his analysis of the Tello object (published in 1975), "attempted to relate the metal to Transcaucasian natural antimony" (i.e. native metal) and that "the antimony objects from Transcaucasia are all small personal ornaments." This weakens the evidence for a lost art "of rendering antimony malleable."
The Roman scholar Pliny the Elder described several ways of preparing antimony sulfide for medical purposes in his treatise Natural History. Pliny the Elder also made a distinction between "male" and "female" forms of antimony; the male form is probably the sulfide, while the female form, which is superior, heavier, and less friable, has been suspected to be native metallic antimony.
The intentional isolation of antimony is described by Jabir ibn Hayyan before 815 AD. A description of a procedure for isolating antimony is later given in the 1540 book De la pirotechnia by Vannoccio Biringuccio, predating the more famous 1556 book by Agricola, De re metallica. In this context Agricola has been often incorrectly credited with the discovery of metallic antimony. The book Currus Triumphalis Antimonii (The Triumphal Chariot of Antimony), describing the preparation of metallic antimony, was published in Germany in 1604. It was purported to be written by a Benedictine monk, writing under the name Basilius Valentinus in the 15th century; if it were authentic, which it is not, it would predate Biringuccio.[note 1]
The metal antimony was known to German chemist Andreas Libavius in 1615 who obtained it by adding iron to a molten mixture of antimony sulfide, salt and potassium tartrate. This procedure produced antimony with a crystalline or starred surface.
The first discovery of naturally occurring pure antimony in the Earth's crust was described by the Swedish scientist and local mine district engineer Anton von Swab in 1783; the type-sample was collected from the Sala Silver Mine in the Bergslagen mining district of Sala, Västmanland, Sweden.
The medieval Latin form, from which the modern languages and late Byzantine Greek take their names for antimony, is antimonium. The origin of this is uncertain; all suggestions have some difficulty either of form or interpretation. The popular etymology, from ἀντίμοναχός anti-monachos or French antimoine, still has adherents; this would mean "monk-killer", and is explained by many early alchemists being monks, and antimony being poisonous.
Another popular etymology is the hypothetical Greek word ἀντίμόνος antimonos, "against aloneness", explained as "not found as metal", or "not found unalloyed". Lippmann conjectured a hypothetical Greek word ανθήμόνιον anthemonion, which would mean "floret", and cites several examples of related Greek words (but not that one) which describe chemical or biological efflorescence.
The early uses of antimonium include the translations, in 1050–1100, by Constantine the African of Arabic medical treatises. Several authorities believe antimonium is a scribal corruption of some Arabic form; Meyerhof derives it from ithmid; other possibilities include athimar, the Arabic name of the metalloid, and a hypothetical as-stimmi, derived from or parallel to the Greek.
The ancient words for antimony mostly have, as their chief meaning, kohl, the sulfide of antimony.
The Egyptians called antimony mśdmt; in hieroglyphs, the vowels are uncertain, but the Coptic form of the word is ⲥⲧⲏⲙ (stēm). The Greek word, στίμμι stimmi, is probably a loan word from Arabic or from Egyptian stm
and is used by Attic tragic poets of the 5th century BC. Later Greeks also used στἰβι stibi, as did Celsus and Pliny, writing in Latin, in the first century AD. Pliny also gives the names stimi [sic], larbaris, alabaster, and the "very common" platyophthalmos, "wide-eye" (from the effect of the cosmetic). Later Latin authors adapted the word to Latin as stibium. The Arabic word for the substance, as opposed to the cosmetic, can appear as إثمد ithmid, athmoud, othmod, or uthmod. Littré suggests the first form, which is the earliest, derives from stimmida, an accusative for stimmi.
The British Geological Survey (BGS) reported that in 2005 China was the top producer of antimony with approximately 84% of the world share, followed at a distance by South Africa, Bolivia and Tajikistan. Xikuangshan Mine in Hunan province has the largest deposits in China with an estimated deposit of 2.1 million metric tons.
|Country||Tonnes||% of total|
Chinese production of antimony is expected to decline in the future as mines and smelters are closed down by the government as part of pollution control. Especially due to a new environmental protection law having gone into effect on January 2015 and revised “Emission Standards of Pollutants for Stanum, Antimony, and Mercury” having gone into effect, hurdles for economic production are higher. According to the National Bureau of Statistics in China, by September 2015 50% of antimony production capacity in the Hunan province (the province with biggest antimony reserves in China) had not been used.
Reported production of antimony in China has fallen and is unlikely to increase in the coming years, according to the Roskill report. No significant antimony deposits in China have been developed for about ten years, and the remaining economic reserves are being rapidly depleted.
The world's largest antimony producers, according to Roskill, are listed below:
(tonnes per year)
|China||Hsikwangshan Twinkling Star||55,000|
|China||China Tin Group||20,000|
|China||Hunan Chenzhou Mining||20,000|
|China||Shenyang Huachang Antimony||15,000|
|South Africa||Consolidated Murchison||6,000|
|Turkey||Cengiz & Özdemir Antimuan Madenleri||2,400|
According to statistics from the USGS, current global reserves of antimony will be depleted in 13 years. However, the USGS expects more resources will be found.
(tonnes of antimony content)
|% of total|
|People's Republic of China||950,000||47.81|
The extraction of antimony from ores depends on the quality and composition of the ore. Most antimony is mined as the sulfide; lower-grade ores are concentrated by froth flotation, while higher-grade ores are heated to 500–600 °C, the temperature at which stibnite melts and separates from the gangue minerals. Antimony can be isolated from the crude antimony sulfide by reduction with scrap iron:
The sulfide is converted to an oxide; the product is then roasted, sometimes for the purpose of vaporizing the volatile antimony(III) oxide, which is recovered. This material is often used directly for the main applications, impurities being arsenic and sulfide. Antimony is isolated from the oxide by a carbothermal reduction:
Antimony has consistently been ranked high in European and US risk lists concerning criticality of the element indicating the relative risk to the supply of chemical elements or element groups required to maintain the current economy and lifestyle.
With most of the antimony imported into Europe and the US coming from China, Chinese production is critical to supply. As China is revising and increasing environmental control standards, antimony production is becoming increasingly restricted. Additionally Chinese export quotas for antimony have been decreasing in the past years. These two factors increase supply risk for both Europe and US.
According to the BGS Risk List 2015, antimony is ranked second highest (after rare earth elements) on the relative supply risk index. This indicates that it has currently the second highest supply risk for chemical elements or element groups which are of economic value to the British economy and lifestyle. Furthermore, antimony was identified as one of 20 critical raw materials for the EU in a report published in 2014 (which revised the initial report published in 2011). As seen in Figure xxx antimony maintains high supply risk relative to its economic importance. 92% of the antimony is imported from China, which is a significantly high concentration of production.
Much analysis has been conducted in the U.S. toward defining which metals should be called strategic or critical to the nation's security. Exact definitions do not exist, and views as to what constitutes a strategic or critical mineral to U.S. security diverge.
In 2015, no antimony was mined in the U.S. The metal is imported from foreign countries. In the period 2011–2014, 68% of America's antimony came from China, 14% from India, 4% from Mexico, and 14% from other sources. There are no publicly known government stockpiles in place currently.
The U.S. "Subcommittee on Critical and Strategic Mineral Supply Chains" has screened 78 mineral resources from 1996–2008. It found that a small subset of minerals including antimony has fallen into the category of potentially critical minerals consistently. In the future, a second assessment will be made of the found subset of minerals to identify which should be defined of significant risk and critical to U.S. interests.
Antimony is mainly used as the trioxide for flame-proofing compounds, always in combination with halogenated flame retardants except in halogen-containing polymers. The flame retarding effect of antimony trioxide is produced by the formation of halogenated antimony compounds, which react with hydrogen atoms, and probably also with oxygen atoms and OH radicals, thus inhibiting fire. Markets for these flame-retardants include children's clothing, toys, aircraft, and automobile seat covers. They are also added to polyester resins in fiberglass composites for such items as light aircraft engine covers. The resin will burn in the presence of an externally generated flame, but will extinguish when the external flame is removed.
Antimony forms a highly useful alloy with lead, increasing its hardness and mechanical strength. For most applications involving lead, varying amounts of antimony are used as alloying metal. In lead–acid batteries, this addition improves plate strength and charging characteristics. For sailboats, lead keels are used as counterweights, ranging from 600 lbs to over 8000 lbs; to improve hardness and tensile strength of the lead keel, antimony is mixed with lead between 2% and 5% by volume. Antimony is used in antifriction alloys (such as Babbitt metal), in bullets and lead shot, electrical cable sheathing, type metal (for example, for linotype printing machines), solder (some "lead-free" solders contain 5% Sb), in pewter, and in hardening alloys with low tin content in the manufacturing of organ pipes.
Three other applications consume nearly all the rest of the world's supply. One application is as a stabilizer and catalyst for the production of polyethylene terephthalate. Another is as a fining agent to remove microscopic bubbles in glass, mostly for TV screens; antimony ions interact with oxygen, suppressing the tendency of the latter to form bubbles. The third application is pigments.
Antimony is increasingly being used in semiconductors as a dopant in n-type silicon wafers for diodes, infrared detectors, and Hall-effect devices. In the 1950s, the emitters and collectors of n-p-n alloy junction transistors were doped with tiny beads of a lead-antimony alloy. Indium antimonide is used as a material for mid-infrared detectors.
Biology and medicine have few uses for antimony. Treatments containing antimony, known as antimonials, are used as emetics. Antimony compounds are used as antiprotozoan drugs. Potassium antimonyl tartrate, or tartar emetic, was once used as an anti-schistosomal drug from 1919 on. It was subsequently replaced by praziquantel. Antimony and its compounds are used in several veterinary preparations, such as anthiomaline and lithium antimony thiomalate, as a skin conditioner in ruminants. Antimony has a nourishing or conditioning effect on keratinized tissues in animals.
Antimony-based drugs, such as meglumine antimoniate, are also considered the drugs of choice for treatment of leishmaniasis in domestic animals. Unfortunately, besides having low therapeutic indices, the drugs have minimal penetration of the bone marrow, where some of the Leishmania amastigotes reside, and curing the disease – especially the visceral form – is very difficult. Elemental antimony as an antimony pill was once used as a medicine. It could be reused by others after ingestion and elimination.
Antimony(III) sulfide is used in the heads of some safety matches. Antimony sulfides help to stabilize the friction coefficient in automotive brake pad materials. Antimony is used in bullets, bullet tracers, paint, glass art, and as an opacifier in enamel. Antimony-124 is used together with beryllium in neutron sources; the gamma rays emitted by antimony-124 initiate the photodisintegration of beryllium. The emitted neutrons have an average energy of 24 keV. Natural antimony is used in startup neutron sources.
Historically, the powder derived from crushed antimony (kohl) has been applied to the eyes with a metal rod and with one's spittle, thought by the ancients to aid in curing eye infections. The practice is still seen in Yemen and in other Arabian countries.
The effects of antimony and its compounds on human and environmental health differ widely. Elemental antimony metal does not affect human and environmental health. Inhalation of antimony trioxide (and similar poorly soluble Sb(III) dust particles such as antimony dust) is considered harmful and suspected of causing cancer. However, these effects are only observed with female rats and after long-term exposure to high dust concentrations. The effects are hypothesized to be attributed to inhalation of poorly soluble Sb particles leading to impaired lung clearance, lung overload, inflammation and ultimately tumour formation, not to exposure to antimony ions (OECD, 2008). Antimony chlorides are corrosive to skin. The effects of antimony are not comparable to those of arsenic; this might be caused by the significant differences of uptake, metabolism, and excretion between arsenic and antimony.
For oral absorption, ICRP (1994) has recommended values of 10% for tartar emetic and 1% for all other antimony compounds. Dermal absorption for metals is estimated to be at most 1% (HERAG, 2007). Inhalation absorption of antimony trioxide and other poorly soluble Sb(III) substances (such as antimony dust) is estimated at 6.8% (OECD, 2008), whereas a value <1% is derived for Sb(V) substances. Antimony(V) is not quantitatively reduced to antimony(III) in the cell, and both species exist simultaneously.
Antimony is mainly excreted from the human body via urine. Antimony and its compounds do not cause acute human health effects, with the exception of antimony potassium tartrate ("tartar emetic"), a prodrug that is intentionally used to treat leishmaniasis patients.
Prolonged skin contact with antimony dust may cause dermatitis. However, it was agreed at the European Union level that the skin rashes observed are not substance-specific, but most probably due to a physical blocking of sweat ducts (ECHA/PR/09/09, Helsinki, 6 July 2009). Antimony dust may also be explosive when dispersed in the air; when in a bulk solid it is not combustible.
The 8-hour time-weighted average (TWA) is set at 0.5 mg/m3 by the American Conference of Governmental Industrial Hygienists and by the Occupational Safety and Health Administration (OSHA) as a legal permissible exposure limit (PEL) in the workplace. The National Institute for Occupational Safety and Health (NIOSH) has set a recommended exposure limit (REL) of 0.5 mg/m3 as an 8 hour TWA. Antimony compounds are used as catalysts for polyethylene terephthalate (PET) production. Some studies report minor antimony leaching from PET bottles into liquids, but levels are below drinking water guidelines. Antimony concentrations in fruit juice concentrates were somewhat higher (up to 44.7 µg/L of antimony), but juices do not fall under the drinking water regulations. The drinking water guidelines are:
Certain compounds of antimony appear to be toxic, particularly antimony trioxide and antimony potassium tartrate. Effects may be similar to arsenic poisoning. Occupational exposure may cause respiratory irritation, pneumoconiosis, antimony spots on the skin, gastrointestinal symptoms, and cardiac arrhythmias. In addition, antimony trioxide is potentially carcinogenic to humans.
Adverse health effects have been observed in humans and animals following inhalation, oral, or dermal exposure to antimony and antimony compounds. Antimony toxicity typically occurs either due to occupational exposure, during therapy or from accidental ingestion. It is unclear if antimony can enter the body through the skin.
|Wikimedia Commons has media related to Antimony.|
|Look up antimony in Wiktionary, the free dictionary.|